CACEM

Category:

CACEM

Overview:

Messages

Main components:

PLA, PBAT, PBS, Talc

Performance introduction:

CACEM01 is an extrusion grade biodegradable resin. Its particles are milky white or light yellow, easy to absorb moisture, and no odor. The biological base content of the product can reach more than 50%, effectively reducing carbon emissions. The straw crystallization molding cycle is short, and there is no obvious deformation after crystallization. The food safety performance of the resin meets the relevant requirements of GB4806, the fluorine content is less than 100ppm, and the biodegradability meets the requirements of international authoritative standards such as EN13432 and ASTMD6400.

Mechanical properties (after annealing)	Test standards	Company	Test result
Tensile strength	ISO 527	MPa	≥30
Elongation at break	ISO 527	%	≥15
Thermal deformation temperature	Test standards	Company	Test result
After crystallization	ASTM D648-2007	°C	≥80
Other	Test standards	Company	Test result
Melt index	ISO 1133	g/10min (190℃，2.16KG)	≦10
Density	ISO 1183	g/cm³	1.30-1.35
Extrusion molding conditions		Company	Recommended value
Temperature at the rear of the barrel		℃	130-150
Temperature in the middle of the barrel		℃	175-185
Temperature in front of barrel		℃	175-185
Die temperature		℃	175-185
Crystallization forming conditions		Company	Recommended value
Oven temperature		℃	85
Molding cycle		min	≧3

Application field:

Biodegradable straw

Storage and packaging:

This product is a biodegradable plastic particle, which should be placed in a dry, ventilated place and kept away from light. It should be used as soon as possible after unpacking. For particles that are not used completely in time after unpacking, they shall be dried at 80 ℃ for 4h in the next use.

key word: Biodegradable modified resin | Biodegradable membrane bags

Address: Qingda Industrial Park, Chengyang District, Qingdao, Shandong

CACEM

About Us

Biodegradable modified resin

Biodegradable membrane bags

CAC BIOMATERIAL