CACBM04

Category:

CACBM

Overview:

Main components：PLA, PBAT
Application area：Biodegradable self sealing bag, biodegradable bone strip
Storage and packaging：This product is a biodegradable plastic particle, which should be placed in a dry, ventilated place and kept away from light. It should be used as soon as possible after unpacking. For particles that are not used completely in time after unpacking, they shall be dried at 80 ℃ for 4h in the next use.

Messages

Main components：

PLA, PBAT

Performance Introduction：

CACBM04 is a blow film grade and extrusion grade biodegradable resin (food grade). The particles are milky white or light yellow, easy to absorb moisture, and the film produced has good gloss, transparency, no odor, good coloring performance, no harmful elements such as Pb, Cd, Hg, Cr, PBB, PBDE, no toxic substances such as o-benzene plasticizer, bisphenol A, etc. The food safety performance meets the relevant requirements of GB4806, The biodegradability meets the requirements of international authoritative standards such as EN13432 and ASTMD6400.

Physical property index of particles
Test items		Test standards	Company	Test result
Fusible finger		ISO1133	g/10min（190℃，2.16kg）	3~5
Density		ISO1183	g/cm³	1.24~1.25
Tensile strength		ISO527	MPa	≧20
Elongation at break		ISO527	%	≧500
Film blowing forming conditions			Company	Recommended value
Drying temperature			℃	60-80
Drying Time			Hr	4-6
Temperature at the rear of the barrel			℃	120-130
Temperature in the middle of the barrel			℃	145-155
Temperature in front of barrel			℃	145-155
Tee temperature			℃	145-155
Die head temperature			℃	145-155
Performance index of blown film (film thickness is about 20 μ m)
Test items		Test standards	Company	Test result
Tensile strength	Transverse	ISO527	MPa	≧30
Tensile strength	Portrait	ISO527	MPa	≧40
Elongation at break	Transverse	ISO527	%	≧700
Elongation at break	Portrait	ISO527	%	≧300
Right angle tear strength		ISO527	kN/m	≧160
Heat sealing strength		ISO527	N/15mm	≧10

Application area：

Biodegradable self sealing bag, biodegradable bone strip

Storage and packaging：

本产品为全生物降解塑料粒子，宜放置于干燥、通风处，且避光保存，拆包后尽快使用。对于拆包后未及时使用完全的粒子，下次使用时要进行烘干处理，烘干温度80℃，烘干时间4h。

key word: Biodegradable modified resin | Biodegradable membrane bags